| Backing | Biaxially Oriented Polypropylene Film | Biaxially Oriented Polypropylene Film | Biaxially Oriented Polypropylene Film | Biaxially Oriented Polypropylene Film | Biaxially Oriented Polypropylene Film | Biaxially Oriented Polypropylene Film | Biaxially Oriented Polypropylene Film |
| Adhesive | Emulsion Pressure Sensitive Water Based Acrylic | Emulsion Pressure Sensitive Water Based Acrylic | Emulsion Pressure Sensitive Water Based Acrylic | Emulsion Pressure Sensitive Water Based Acrylic | Emulsion Pressure Sensitive Water Based Acrylic | Emulsion Pressure Sensitive Water Based Acrylic | Emulsion Pressure Sensitive Water Based Acrylic |
| Total Thickness | 40μ | 43μ | 45μ | 47μ | 50 | 54 | 65 |
| Film Thickness | 25μ | 25μ | 25μ | 25μ | 28μ | 28μ | 40μ |
| Adhesive Thickness | 15μ | 18μ | 20μ | 22μ | 22μ | 26μ | 25μ |
| 180 Peel Adhesion (ASTM D 3330) | 450g/in | 490g/in | 520g/in | 540g/in | 560g/in | 620g/in | 730g/in |
| Holding Power (ASTM D 3654) | 5 min | 5 min | 10 min | 10 min | 20 min | 20 min | 20 min |
| Tensile Strength (ASTM D 3759) | 14kg/mm | | 7500 | | | | 0.06% |
| Elongation (ASTM D 3759) | | | 0 | | | | 0.00 |
| Initial Tack (JIS Z0237) | <70 mm | <60 mm | <50 mm | <50 mm | <35 mm | <35 mm | <35 mm |